Effect of Disinfection on the Bond Strength between Denture Teeth and Microwave-Cured Acrylic Resin Denture Base.

PURPOSE: Denture tooth debonding is a common complication for denture wearers; however, the effect of complete denture disinfection on bonding between denture teeth and acrylic resin remains unclear. The aim of this study was to evaluate the effect of disinfection methods on the bond strength between denture teeth and microwave-cured acrylic resin denture base. MATERIALS AND METHODS: Three commercial brands of denture teeth (Trilux, Biolux, Vipi Dent Plus) and one microwave-cured acrylic resin denture base were tested. Each brand of denture teeth was divided into seven groups (n = 6; estimated by partial Eta squared). The specimenss of groups H and Cl were immersed in 1% sodium hypochlorite and 4% chlorhexidine digluconate for 7 days, respectively. In group Br, the specimens were subjected to toothbrush simulation under 200 g of force for 20,000 cycles. In groups Br-H and Br-Cl, the specimens were brushed and further disinfected with 1% sodium hypochlorite and 4% chlorhexidine digluconate, respectively. In control groups 1 (Co1) and 2 (Co2), the specimens were stored in distilled water for 50 ± 2 hours and 7 days, respectively. Shear bond strength testing was performed at the resin/tooth interface in a universal testing machine at a 1 mm/min crosshead speed. The failure pattern was quantified and classified into adhesive, cohesive, or mixed. Data were analyzed using two-way ANOVA and Tukey HSD test (α = 0.05). RESULTS: Disinfection with 1% sodium hypochlorite (p = 0.031), brushing (p < 0.0001), and association of brushing with either 1% sodium hypochlorite (p < 0.0001) or 4% chlorhexidine digluconate (p = 0.01) reduced the bond strength between denture teeth and microwave-cured acrylic resin denture base. All commercial brands of denture teeth presented a similar bond strength (p > 0.05). The failure pattern was predominantly adhesive independent of the disinfection method and denture tooth brand. CONCLUSIONS: Disinfection with sodium hypochlorite, brushing, and the association of mechanical and chemical methods reduced the bond strength between denture tooth and microwave-cured acrylic resin denture base.

Three-species biofilm model onto plasma-treated titanium implant surface.

In this study, titanium (Ti) was modified with biofunctional and novel surface by micro-arc oxidation (MAO) and glow discharge plasma (GDP) and we tested the development of a three-species periodontopatogenic biofilm onto the treated commercially-pure titanium (cpTi) surfaces. Machined and sandblasted surfaces were used as control group. Several techniques for surface characterizations and monoculture on bone tissue cells were performed. A multispecies biofilm composed of Streptococcus sanguinis, Actinomyces naeslundii and Fusobacterium nucleatum was developed onto cpTi discs for 16.5h (early biofilm) and 64.5h (mature biofilm). The number of viable microorganisms and the composition of the extracellular matrix (proteins and carbohydrates) were determined. The biofilm organization was analyzed by scanning electron microscopy (SEM) and Confocal laser scanning microscopy (CLSM). In addition, MC3T3-E1 cells were cultured on the Ti surfaces and cell proliferation (MTT) and morphology (SEM) were assessed. MAO treatment produced oxide films rich in calcium and phosphorus with a volcano appearance while GDP treatment produced silicon-based smooth thin-film. Plasma treatments were able to increase the wettability of cpTi (p<0.05). An increase of surface roughness (p<0.05) and formation of anatase and rutile structures was noted after MAO treatment. GDP had the greatest surface free energy (p<0.05) while maintaining the surface roughness compared to the machined control (p>0.05). Plasma treatment did not affect the viable microorganisms counts, but the counts of F. nucleatum was lower for MAO treatment at early biofilm phase. Biofilm extracellular matrix was similar among the groups, excepted for GDP that presented the lowest protein content. Moreover, cell proliferation was not significantly affected by the experimental, except for MAO at 6days that resulted in an increased cell proliferative. Together, these findings indicate that plasma treatments are a viable and promising technology to treat bone-integrated dental implants as the new surfaces displayed improved mechanical and biological properties with no increase in biofilm proliferation.

Production of a biofunctional titanium surface using plasma electrolytic oxidation and glow-discharge plasma for biomedical applications.

In this study, the authors tested the hypotheses that plasma electrolytic oxidation (PEO) and glow-discharge plasma (GDP) would improve the electrochemical, physical, chemical, and mechanical properties of commercially pure titanium (cpTi), and that blood protein adsorption on plasma-treated surfaces would increase. Machined and sandblasted surfaces were used as controls. Standard electrochemical tests were conducted in artificial saliva (pHs of 3.0, 6.5, and 9.0) and simulated body fluid. Surfaces were characterized by scanning electron microscopy, energy-dispersive spectroscopy, x-ray photoelectron spectroscopy, atomic force microscopy, x-ray diffraction, profilometry, Vickers microhardness, and surface energy. For biological assay, the adsorption of blood serum proteins (i.e., albumin, fibrinogen, and fibronectin) was tested. Higher values of polarization resistance and lower values of capacitance were noted for the PEO and GDP groups (p < 0.05). Acidic artificial saliva reduced the corrosion resistance of cpTi (p < 0.05). PEO and GDP treatments improved the surface properties by enrichment of the surface chemistry with bioactive elements and increased surface energy. PEO produced a porous oxide layer (5-µm thickness), while GDP created a very thin oxide layer (0.76-µm thickness). For the PEO group, the authors noted rutile and anatase crystalline structures that may be responsible for the corrosion barrier improvement and increased microhardness values. Plasma treatments were able to enhance the surface properties and electrochemical stability of titanium, while increasing protein adsorption levels.

Surface treatment influences electrochemical stability of cpTi exposed to mouthwashes.

The role of surface treatment on the electrochemical behavior of commercially pure titanium (cpTi) exposed to mouthwashes was tested. Seventy-five disks were divided into 15 groups according to surface treatment (machined, sand blasted with Al2O3, and acid etched) and electrolyte solution (artificial saliva ­ control, 0.12% chlorhexidine digluconate, 0.05% cetylpyridinium chloride, 0.2% sodium fluoride, and 1.5% hydrogen peroxide) (n = 5). Open-circuit-potential and electrochemical impedance spectroscopy were conducted at baseline and after 7 and 14 days of immersion in each solution. Potentiodynamic test and total weight loss of disks were performed after 14 days of immersion. Scanning electron microscopy, energy dispersive spectroscopy, white light interferometry and profilometry were conducted for surface characterization before and after the electrochemical tests. Sandblasting promoted the lowest polarization resistance (Rp) (P b .0001) and the highest capacitance (CPE) (P b .006), corrosion current density (Icorr) and corrosion rate (P b .0001). In contrast, acid etching increased Rp and reduced CPE, independent to the mouthwash; while hydrogen peroxide reduced Rp (P b .008) and increased Icorr and corrosion rate (P b .0001). The highest CPE values were found for hydrogen peroxide and 0.2% sodium fluoride. Immersion for longer period improved the electrochemical stability of cpTi (P b .05). In conclusion, acid etching enhanced the electrochemical stability of cpTi. Hydrogen peroxide and sodium fluoride reduced the resistance to corrosion of cpTi, independent to the surface treatment. Chlorhexidine gluconate and cetylpyridinium chloride did not alter the corrosive behavior of cpTi.